WL-AD203 Epoxy resin
| Appearance | Milky white liquid |
| Non-volatile matter (Wt, %) | 53±2 |
| Viscosity(mPa.s)(25℃) | 500 ~ 8000 |
| Epoxy equivalent (supplied form) (g/Eq) | 1010±50 |
WL-AD203 is a water-based epoxy dispersion. When used with the recommended water-based epoxy curing agent, it can be used to prepare high-performance water-based epoxy coatings, designed for anti-corrosion primers and epoxy floor paints for various metal substrates
Features: fast surface drying, suitable for various wet-on-wet matching processes, rapid hardness build-up, long application period
WL-AC040 Epoxy curing agent
| Item | Value | Testing Method |
| Appearance | Light yellow transparent liquid | Visual |
| Non-Volatile content(%) | 40±2 | GB/T 1725-2007 |
| Viscosity(mPa.s)(25℃) | 2000~8000 | GB/T 21059-2007 |
| Active hydrogen equivalent | 300±10 | ---- |
WL-AC040 is a water-soluble modified polyamine adduct, recommended for use with waterborne epoxy resin, designed for anti-corrosion primers and epoxy floor paints for various metal substrates.
Features: fast curing speed, short surface drying time, excellent adhesion, long application period, and extremely high cost performance
WL-SP1000 is a water-based emulsion of acrylic copolymer.
Features: excellent gloss, excellent initial water resistance, good water resistance, strong versatility, suitable for primer and topcoat of various metal substrates.
| Item | Value | Testing Method |
| Appearance | Milky white liquid | Visual |
| Non-Volatile content(%) | 47±1 | GB/T1725-2007 |
| Viscosity(mPa.s)(25℃) | 50~500 | GB/T 21059-2007 |
| PH | 7.0~9.0 | GB/T 9724-2007 |
| Minimum film forming temperature (°C) | 40 | - |
A set of coating test data consisting of WL-AD203 epoxy/WL-AC040 curing agent primer + WL-SP1000 single component topcoat