WL-K173 is a self-crosslinking modified epoxy dispersion, recommended for metal and the substrates are not easy to adhere to, and for application that with high requiement for salt spray resistance.

Physical Propert

Appearance	White milky emulsion
Solid content	42±2
Viscosity (cps∕25℃)	2000-10000
pH	8-10

Performance

1 Excellent salt spray resistance

2 Excellent drying speed and hardness

3 Good film formation and high gloss

4 Excellent water resistance and corrosion resistance

7 Good pigment dispersion, can participate in grinding color paste

8 Can be used in one-component coatings without adding curing agent

Good Salt Spray Resistance Self-Crosslinking Modified Epoxy Resin For Metal Coating

Application

Used in corrosion-resistant metal industrial coatings, marine coatings, heavy duty anticorrosive coatings, especially suitable for metal anticorrosive primers.

Used in one-component self-drying coatings, and the performance will be enhanced by baking at 80℃ if the condition permits.

Used with acrylic emulsion, polyurethane dispersion, PUA, etc., but it should be determined by experiment before use.

Storage

Store in a cool, ventilated and dry place at 5-40℃, protected from light and sealed;

Packing

200kgs/barrel,1000kgs/IBC

Special Tips

This material is complied according to our existing technology and experience, the technical

advice provided is sincere, but it is not guaranteed to be used in all samples and formulations,

all the data are for users reference only.